聚醚型与聚酯型聚氨酯弹性体的性能研究.pdf

第4卷第2期
塑料工业
2013年2月
CHINA PLASTICS INDUSTRY
87?
聚型与聚隃型聚筼酯弹性体的性能研究
张敏,夏青,王吴,张宝峰,李猛
(陕西科技大学教育部轻化工助剂化学与技术重点实验室,陕西西安710021)
摘要:使用聚乙二醇(PEG)、聚四亚甲基醚二醇(PIMG)、聚己内酯(PCL)和4,4'-二苯基甲烷二异氰酸酯
(MD)合成了聚醚多元醇型和聚酯多元醇型热塑性聚氨酯弹性体(TPC)。研究了各种TPU中异氰酸酯指数(Ro)、
硬段浓度(C)、聚醚和聚酯的种类、摩尔质量及原料用量等对弹性体力学性能的影响;并且使用双酚A型环氧树脂
NPEL127改性了弹性体的耐热性。研究结果表明:TPU的硬度随着R。和C的增加而增加;聚瞇型TPU中,随着软
段中柔性链的增加,TPU的硬度下降而力学性能提高;聚酯型TPU中,随着聚酯和聚酯二元醇摩尔质量的提高,TPU
的硬度和力学性能均有提高;聚酯型TPU的力学性能优于聚醚型TPU;环氧树脂改性使得聚酵型TPU耐热性提高。
关键词:聚氨酯弹性体;聚酯型;聚谜型;改性;耐热性
DOI:10.3969/j.isn.1005-5770.2013.02.022
中图分类号:TQ323.8
文献标识码:B
文章编号:1005-5770(2013)02-0087-03
Study on Properties of Polyether and Polyester Polyurethane Elastomer
ZHANG Min, XIA Qing, WANG Hao, ZHANG Bao-feng, LI Meng
( Shaanxi University of Science and Technology, Key Laboratory of Iight Industry and Chemical Auxiliary Chemistry and
Technology, Ministry of Education, Xi'an 710021, China
Abstract: The thermoplastic polyurethane elastomer(TPU was synthesized using polyether polyol of
polyethylene glycol(PEG), poly(tetramethylene ether )glycol( PTMG), polyester polyol polycaprolactone
(PCL)and 4, 4'-diphenylmethane diisocyanate (MDI). The effect of isocyanate index (R), hard
segment concentration (C, and type, molecular weight and amount of polyether polyol on the performance
of polyurethane elastomer were studied. In addition, the bisphenol A epoxy resin NPEL-127 were used to
modifed the polyure hane elastomer n order o mprove its eat resistance. The results showed that: the harness
of TPU increases with increasing R and C; with the increase of molecular weight of the polyester and polyester
diol, the hardness and mechanical properties of TPU was improved; the mechanical properties of polyester TPU
was better than that of polyether TPU; the heat resistance of TPU modified by epoxy resin was improve
Keywords: Polyu
le Elastomer; Polyester; Polyether; Modification; Heat Resistance
聚氨酯弹性体(TPU)中由于软硬段的不相容(PCL)为原料合成热塑性TPU。研究了热塑性TPU
性,存在明显的微相分离结构,具有优良的综合力学中聚瞇/酯多元醇摩尔质量、聚醚/酯种类及用量、异
性能?-4。环氧树脂是一种热固性树脂,聚醚型TPU氰酸酯指数(R。)和硬段浓度(C1)对TPU性能的
分子主链的结构中有柔性的一C-0C一链,与双酚影响;并且使用双酚A型环氧树脂NPEL-127改性聚
A型环氧树脂有良好的相容性,且环氧树脂重复单元醚型TPU,以提高其耐热性。
上所含的羟基能够与异氰酸酯基反应,从而在TPC1实验部分
长链中引人含有耐热性较好的双酚A环氧树脂基团,1.1实验原料
可以提高聚瞇型TPU的耐热性。
MDl:工业级,德国巴斯夫公司;PEG:工业
本研究采用一步法ら?,以4,4'-二苯基甲烷品,摩尔质量分別为400、38001000200gmo,
二异氰酸酯(MDI)、聚醚多元醇聚乙二醇(PC)、江苏太平洋化学有限公司;PCL:工业品,摩尔质量
聚四亚甲基醚二醇(PTMG)和聚酯多元醇聚己内酯
陕西科技大学科研创新团队项目资助(TD10-01)
作者简介:张敏,女,教授,博士,博士生导师,研究方向为可生物降解高分子材料的合成、降解和机理研究。
yanjiushi206@ 163. cor