高碳铬不锈轴承钢孪晶碳化物硏究
汪红晓
(攀长特公司质量计量中心,四川江油621704
摘要:研究了高碳铬不锈轴承钢“孪晶碳化物”(直线状和链状碳化物)的影响因素及形成原因,结果表明:加
热温度达到1140℃,退火后开始出现沿品界分布的链状碳化物;加热温度≥1160℃,退火后出现大量直线状和
链状两种形态的破化物。材料从高温直接冷却时,温度≥1080℃并且冷却速度≤80℃h可能析出链状碳化物,
并且温度越高冷却速度越慢析出的可能性就越大。直线状碳化物形成原因为:材籵加热温度过高,晶粒长大的
过程中晶界迁移时侷然发生堆垛错误形成了生长孪晶,在随后的退火过程中碳化物向奧氏体孪晶界面沉淀而形
成,是真正意义上的孪晶碳化物。链状碳化物是由于材料过热或者局部过热;在随后冷却过程中碳化物沿奥氏
体晶界析出而形成的,本质上是一种网状碳化物。
关键词:高碳铬不锈轴承钢;孪晶碳化物;加热温度;直线状碳化物;链状碳化物
中图分类号:TG15.21;TG142.1+1文献标识码:A文章标号:1674-0971(2011)04-009-07
Research on Twin Carbide in High Carbon Chromium
Stainless Bearing Steel
Wang Hongxiao
( Metering and Measuring Department, Sichuan Changcheng Speial Steel Co, Ltd, Pangang Group.Jiangyou, Sichuan 621704
Abstract: In this paper, the effecting factors and reasons for twin and carbide straighe line and chain carbide)in high
carbon chromium stainless bearing steel were researched. The results showed that when the heating temperture reaches 1
140 chain carbides c ue along rain boundary after annealing when the heating tempera ure =1 160 C. a large number
of straight line and chain carbides occurre after annealing: when the material is directly cooled from high temperature,
precipitation of chain carbides is possible if temperature =1080 C and cooling speed 80 Ch. The higher the temperatur
and the slower the cooling speed, the more possible the precipitation is The reasons for formation of straight line carbide are
as follows: the heating temperature is extremly high and stacking fault occures accidentally at the time of grain boundary
migration in the process of grain growth, which results in precipit ation of carbide in austenite twin boundary in subsequent
annealing and forms the real sense of twin carbide; chain carbides are formed by the precipitation of carbides along austenite
grain boundary due to the material overheating or localized overheating, which substantially is a kind of carbide network
Keywords: High carbon chromium stainless bearing steel, Twin carbide, Healing temperature, Straight line
carbide. Chain carbide
前言
化物合格率一直比较低,其他特钢企业的也是如
此。因此特钢企业不愿意生产该品种,轴承企业订
9Cr18、9Cr18Mo属于高碳铬不锈轴承钢,具有货困难。根据轴承用户的要求,在检验中直线状和
高的硬度,并有不锈、耐蚀的性能,常用于制作军链状两种形态的碳化物都被认定是李晶碳化物。
工.、航空、航天和航海等高级轴承。该钢种常用的但是特钢企业和轴承企业对李晶碳化物的形成机
标准为GBmT3086《高碳铬不锈轴承钢技术条件》和理、形貌和评定原则都还有分歧。大致有以下三种
CJX-S027-2005,这两者都要求检验孪晶碳化物。意见:(1)只有直线状的碳化物才是李晶碳化物,根
多年以来攀长钢公司高碳铬不锈轴承钢的孪晶碳据是孪晶界是一条直线;(2)两条以上的平行线才
收件日期:2011-09-17
作者简介;汪红晓(1975-)2男,工程师,河南省南阳市人.1998年毕业于武汉科技大学金属材料与热处理专业,现从事物理检测方面的管理工作,
就职于攀钢集团四川长城特殊钢公司计量检测中心理化检验四车间.联系电话:3887012E-mail:fengzi1182006@yahoo.com.cm