SDS/正丁醇/正庚烷/水微乳液稳定性分析及应用
王军正,熊徳元1,刘雄民,莫炳荣,陈琼霞
(1.广西大学化学化工学院,广西南宁530004;2.广西化工研究院,广西南宁530001)
摘要:研究了十二烷基硫酸钠(SDS)/正丁醇/正庚烷/水(或氯化镁与硝酸铝混合水溶液或氢氧化钠溶液)四组
分形成稳定徽乳液的条件。考察了表面活性剂与助表面活性剂的质量比、温度、pH值、盐浓度对该体系稳定性的
影响及水与表面活性剂的摩尔比(o。)对水核粒径的影响。结果表明,ms:m(丁,=4:6时,反相徽乳液最稳
定,对温度变化不敏感,pH值为7~13时,具有较好的稳定性,随着镁铝混合盐溶液浓度的增加,反相微乳区城急
剧缩小,水核粒径随着。增大而增大,在稳定徽乳液区域内制备了分布较均匀,尺寸范圃30~70mm的粒状纳米
颗粒。
关键词:微乳液;纳米颗粒;稳定性因素
中图分类号:TQ423.11;TQ132.2;0648.23文献标识码:A文章编号:1671-3206(2011)09-1522-03
Stability analysis and application of SDS/N-butanol/n-heptane
water microemulsion system
WANG Jun-zheng XIONG De-yuan, LIU Xiong-min MO Bing-rong,CHEN Qiong-oia
( 1. School of hemistry and Chemical Engineering, Guangxi University, Nanning 530004, China
2. Guangxi Research Institute of Chemical Industry, Nanning 530001, China
Absract: The formation of microemulsion system of sodium dodel sul ate(SDS)/n-butano/n-hepta-
e water [or Mgcl, 6H, O and Al(NO: )3 9H O mixed aqueous solution or NAOH solution] were stud
ied. The influences of the mass ratio of surfactant to assistant, temperature, PH value and salinity to the
systems and the influences of the molar ratio of water to surfactant(a )to the sizes of the micelles were
investigated. It was found that m(sos] m(butanol) was 4: 6, the microemulsion system was stable phase
glons, whi
ich was insensitive for temperatures and not changed with PH value from 7 to 13, ut the stable
phase region of the microemulsion became smaller with increasing salinity(Mg, Al sultion). The sizes of
the micelles increased with increasing w. Nano-particles were prepared in the stable phase regions and
had a narrow size distribution, the sizes were from 30 nm to 70 nm.
Key words: microemulsions; nano-particles; stability factors
微乳液法是20世纪80年代兴起的一种有效的正庚烷/水徴乳液的性质,而对该四元体系的稳定性
制备纳米材料的方法。该方法具有工艺简单、易于的研究报道较少。本文重点研究了SDS/正丁醇/正
操作、粒径大小可控、粒度分布均匀、粒子分散性好庚烷/水溶液四组分W/O微乳液能够稳定存在的
等特点?。近年来,人们运用徽乳液法制备出多种组成范围,考察了温度、pH值、盐浓度等因素对该体
纳米材料3。但不同微乳液体系的稳定区域不同
,系稳定性的影响,并应用该体系制备了纳米粒子。
且微乳区域的大小决定了微乳液溶水量的大小,对
1实验部分
制备纳米粒子时反应物的配比和反应条件有重要影
响,因而使用前均需对其稳定性、微乳区域范圃及水1.1试剂与仪器
核尺寸进行研究5?。
MgCl2-6H120、Al(NO3)39H20、NaOH、Na2CO3、
冯广卫门测定了SDS/正丁醇/正庚烷水微乳正丁醇、正庚烷均为分析纯;十二烷基硫酸钠
液体系的结构参数,冯建等?研究了SDS/正丁醇/(SDS),化学纯;二次蒸馏水,自制。
收稿日期:2011-07-08修改稿日期:2011-07-13
基金项目:广西科学基金资助项目(桂科自0832193)
作者简介:王军正(1984-),男,河南驻马店人,广西大学在读硕士研究生,师从熊德元教授,从事无机材料方向的研究。
电话:15289675895,E-mail:wj-200418@163.com