再生混凝土力学性能试验研究.pdf

孙晓雪等:再生混凝土力学性能试验研究
再生混凝士力学性能试验研究
孙晓雪,赵吉坤,张晓敏
(南京农业大学工学院,南京210031)
【摘要】通过对三种不同配合比的再生混凝土进行强度试验,研究了再生粗骨料取代率分别为0、40%
70%、100%时,再生混凝土的抗压强度与劈裂抗拉强度变化规律,提出了劈裂抗拉强度与抗压强度的关系式。研
究结果表明,随着取代率的增大,混凝土抗压强度与劈裂抗拉强度均呈下降趋勢,但当取代率为70%时,强度反而
有一定上升
【关键词】再生混凝土;劈裂抗拉强度;取代率
【中图分类号】TU528.04
【文献标识码
【文章编号)1001-6864(2012)02-0011-03
STUDY OF MECHANICAL PROPERTIES OF RECYCLED CONCRETE
SUN Xiao-xu. ZHAO Ji-kun, ZHANG Xiao-min
College of Engineering, Nanjing Agricultural University, Nanjing 210031, China
Abstract By testing strength of three kinds of recycled concrete with different mix proportions, we
studied the variation law of compressive strength and splitting tensile strength of recycled aggregate con
crete while the replacement rates of recycled course aggregate are 0, 40%, 70% and 100%. The results
indicate that the compressive strength and splitting tensile strength of concrete decrease with the increase
of replacement rate. However, when the replacement rate is 70%, the strength increase
Key words: recycled aggregate concrete; splitting tensile strength; replacement rate
近年来,我国每年产生大量的建筑垃圾,数量已占普通河砂,细度模数为2.77;水:自来水;天然粗骨料
到城市垃圾的30%~40%,其中50%-60%为废弃混连续级配的碎石,最大粒径为25m;再生粗骨料:南
凝土。国内外一些学者研究了再生混凝土的基本京市浦口区向阳桥房屋拆除废弃混凝土,采用人工破
性能2-4。 Rajkumar B.9的研究表明在用水量相同碎,最大粒径为25m。参照《普通混凝土用砂、石质
的情况下,再生混凝土较基准混凝土坍落度减小,流动量及检验方法标准》,测试了天然粗骨料及再生粗骨
性变差,粘聚性和保水性增强。李佳彬等?系统测试料的基本性能,结果见表1。
了再生粗骨料的基本特性,研究了不考虑与考虑再生
表1
粗骨料的高吸水特性时再生混凝土的基本性能。但是
粗料的甚本性能
针对再生混凝土劈裂抗拉强度与抗压强度关系的研
骨料类数粒径范围堆积密度表观密度吸水率压碎指标
究还比较少。
/mm/kg?mn-3/kg
%
/%
文中通过对三种配合比的再生混凝土进行研究,
天然
5~26.51410
2550
0.51
测试了再生粗骨料取代率分别为0、40%、70%、100%
再生
5~26.51098
2082
6.2517,65
时,再生混凝土的抗压强度与劈裂抗拉强度变化规律,
并提出了劈裂抗拉强度与抗压强度的关系式。对再生1.2混凝土配合比设计
混凝土劈裂抗拉强度与抗压强度的相关性研究进行
为了研究再生粗骨料对混凝土基本性能的影响,
了补充。
试验中再生粗骨料取代率分别为0(普通混凝土)、
试验设计
40%、70%、100%。三种普通混凝土水灰比分别为
1.1试验原材料
0.61、0.49、0.43。试件分别用RC-X-1,RC-X-2、
水泥:南京海螺水泥有限公司生产的海螺牌RC-X-3表示(X为取代率,取值为0、40、70、100)。
32.5R普通硅酸盐水泥,表观密度为3100kg/m3;砂:各混凝土的配合比见表2。
「基金项月]江苏省自然科学基金(BK2010457);国家大学生创新性实验计划项目(101030737);南京农业大学SRT资助项目
(1015A04