T91和P9取热管异种钢焊接
王菊茹,王丽红2,魏广权
(1.营口庆营石化设备有限公司,辽宁营ロ115004;2.沈阳东方钛业有限公司,辽宁沈阳110016
摘要:分析191、P取热管的焊接性能,针对其淬硬性强,冷裂纹倾向大的特点,米取焊前预热、严格控制层间温度、
坪后及时消氢等工艺措施,避免冷裂纹产生,确保焊接接头性能,并成功应用在生产实践中。
关健浔:191;P9;淬硬性;冷裂纹
中图分类号:TC42
文献标识码:B
文章编号:1006-4414(2011)03-0163-02
Heating removing tube T1,P9 dissimilar steel welding
Wang Ju-ru Wang Li-hong, Wei Guang-quan
1. Yingkou Qingying petrochemical eguipment Co. Ltd, Yingkou Liaoning 115004, China
2. Shenyang dongfang titanium industry Co., Ltd, Shenyang Liaoning 110016, China)
Abstract The welding performance of heat removing tube is analyzed. As the tube's hardenability is very strong and colding
cracks tendency is big, aiming at these characteristics, the ef ective process measures must be adopted and including the pre
heat before welding, layer temperature strictly controlling, immedately relieving hydrogen treatment after welding and so on
Thus it can avoid cold crack, ensure the performance of welding joint and is successfully applied in the production practice
Key words: T91; P9 hardenability; cold crack
191和P9材料可焊性分析
2焊接方法和焊接材料选择
某公司制烯烃装置中,反应器内取热管材质为
因管直径较小、管壁较簿,打底层采用CTAW手
ASME SA213MT91和 ASME SA335MP9,规格q14×工钨极弧焊,其余层采用SMAW焊条电弧焊的方
8.56。管内介质为甲醇,管内、外最高工作温度为法。焊材均为日本神钢生产,CTAW焊丝TG-S9CM,
86℃/550℃。在此介质和高温工况下,191与P門异焊条CM-9,其化学成分及力学性能见表3。
种钢焊接接头质量尤为重要。
3焊接工艺评定
P9钢为中合金马氏体耐热钢,在高温下能够保3.1坡口加エ
持良好的化学稳定性和热稳定性。91钢是在
坡口用机械方法加工,坡口表面无裂纹、分层、夹
9 Crl Mo钢基础上开发起来的马氏体热强钢,该钢特杂物等缺陷。坡口形式及尺寸见图1。
点是在9Cr1Mo中加人少量的V、Nb,控制N和Al并
降低C含量。具有高温强度高、抗氧化性能和抗蠕
变性能好等特点。191、R門化学成分和力学性能见
表1、2。但191、P9均有较高的淬硬倾向和冷裂纹倾
向,容易产生高硬度马氏体组织致使接头脆性增加,
产生冷裂纹。因此须采用合理的焊接工艺方案,避免
2,5-3
冷裂纹产生,以保证焊接接头质量。
图1坡口形式及尺寸图
表1T91钢和P9钢化学成分
wt%0
C
M
Si
Nb
N
191标准值0.08~0.120.30~0.600.20-0.50≤0.0≤0.0108.0~9.50.85~1.06≤0.400.06~0.100.18~0.25≤0.040.03~0.07
实测值0.10
0.36
0.300.0110.0058,
0.91
0.20.0070.04
P9标准值≤0.150.30-0.600.25~1.0≤0.025≤0.0258.0-10.00.9~1.1
实测值
0.10
0,420.010.0048.74
1.01
收稿日期:2011-05-09
作者简介:王菊茹(1974-),女,辽宁抚顺人,工程师,主要从事压力容器焊接工作。
163