不同表面处理的钛白粉在色母粒中的应用.pdf

塑料工业
第40卷第11期
96
CHINA PLASTICS INDUSTRY
2012年11月
不同表面处理的钛白粉在色母粒中的应用
陈新红
(攀钢集团研究院有限公司,钒钛资源综合利用国家重点实验室,四川攀枝花617000)
摘要:采用不同的有机处理剂对钛白粉进行表面处理,找到了一种最适合塑料专用钕白粉的有机处理剂。用动态
毛细管法表征处理前后钛白粉的表面亲油性能,并采用红外光谱分析了处理前后钛白粉的结构变化。结果表明,经表
面处理后的钛白粉在加工色母粒过程中,其分散性和着色力都得到了提高
关键词:钛白粉;表面处理;色母粒
DOI:10.3969/issn.1005-5770.2012.11.025
中图分类号:TQ314.263
文献标识码:B
文章编号:1005-5770(2012)11-0096-03
Difference Surface Treatment to Titanium Dioxide and Its Application to Masterbatch
CHEN Xin-hong
( Pangang Group Research Institute Co, Ltd. State Key Laboratory of Vanadium and Titanium Resources Comprehensive Utilization
Panzhihua 617000. China
Abstract: By using different or anic agents for surface treatment of titanium dioxide, the most suitable
organic agent for plastic special titanium dioxide was found out. And the dynamic capillary law was used to
ascertain the transformation of its surface before and after treatment. The IR means was adapted to contrast the
structure of Tio. The results showed that the dispensability and covering capability of Tio, masterbatch in
plastic were both improved in the process
Keywords Titanium Dioxide; Surface Treatment; Colour Masterbatch
钛白粉(二氧化钛)是最重要的白色颜料之
间的界面作用。此种方法处理后的钛白粉与塑料之间
广泛应用在涂料、塑料、造纸、油墨与合成纤维等领的相容性更好,分散性能和着色力得到有效的提高
域中。塑料作为铁白粉的第二大用户,除了利用它的1实验部分
高遮盖力、高着色力及其他颜料性能之外,它还能提
1.1主要原料及设备
高塑料制品的耐热、耐光、耐候性。但是,未经表面
处理的钛白粉含有大量的表面羟基,具有强极性,易
金红石型钛白粉:工业级,攀钢集团钛业有限公
团聚,影响其在应用体系中的分散,最终影响塑料司;硅烷偶联剂A、B:市售;专用钛白粉有机处理
品的质量。只有在充分分散之后,才能达到最佳的使
剂(硅烷偶联剂)C:市售;低密度聚乙烯:50A,
用效果。
北京燕山石化公司;聚乙烯蜡:北京化工大学精细化
目前,钛白行业通常采用硅烷偶联剂、钛酸酯偶
联剂等对钛白粉进行表面处理,偶联剂含有两个不同1.2设备及仪器
性质的基团,一个是亲水基团,与无机物有较好的相
双螺杆挤出机:TSSJ,成都晨光众益科技有限公
容性;另一个是亲油的有机基团,与有机物具有较好司;橡胶试验密炼机:上海科创橡塑机械设备有限公
的相容性,从而达到提高钛白粉的亲油性。但是在这司;积分球式分光光度仪:SP0系列,美国爱色丽
种处理方法下,钛白粉与偶联剂之间作用力不强,并股份有限公司;红外光谱仪: TENSOR27,瑞土布鲁
且混合的均匀性差,不能充分发挥偶联剂的作用。本克光谱仪器公司;扫描电子显微镜(SEM):JSM
研究通过偶联剂的水解基团水解,水解后的一端可与5900LV,日本电子株氏会社。
钛白粉的表面羟基进行缩合反应,使偶联剂与钛白粉1.3工艺路线
之间形成分子键作用力,大大改善钛白粉与有机物之1.3.1钛白粉的表面处理
作者简介:陈新红,男,1980年生,从事钛白粉生产及应用技术研究。chenxinhong990@sina.com