水泥基灌浆料适用水泥试验分析.pdf

2013年第34卷第3期
doi:10.3963/j.issn,1674-6066,2013.03.001
水泥基灌浆料适用水泥试验分析
彰鹏飞
(度门市宏业工程建设技术有限公司,厦门361000
摘要:以硫铝酸盐水泥RSAC425分别换比例替代建酸盐水泥P.O42,5、P.O42.5R、P.O52.5、P.O52.5R,
试验分析其初始流动度、30min流动度保留值及1d、3d、28d抗压强度。试验结果表明,硫铝酸盐水泥RSAC425
分別接比例替代P.O水泥对初始流动度彩响不大,替代P.O42.5水泥、P.O42.5R水泥、P.O52.5水泥超过50%
时,使得浆料30min流动度保留值急剧下降,替代P.O52.5R水泥超过65%时,使得業料30min流动度保留値急剧
下降;硫铝酸盐水泥RSAC425分别接比例替代P.水泥对抗压强度的形响均表现为提高1d、3d强度,降低28d
强度,对快硬性水泥降低28d强度度稿小,对非快硬性水泥强度降低校大
关鍵词:灌浆料;水泥;适应性
Study on the Cement of Cementitious Grout
PENG Peng-fei
(Xiamen Hongye Project Building Technique Co, Itd, Xiamen 361000, China)
Abstract: Using sulphoaluminate cement R SAC 425 to replace Por land cement in proportion to P. O 4.5, P. O
42.R, P.O 52.5, P.O 52. 5R, the initial fluidity, 30 min fluidity retention and I d, 3 d, 2d compressive strength
were studied The test esults showed that sulphoaluminate cement R SAC425 respectively replaced P. O cement in
proportion had little effect on the initial fluidity; the replacing of PO4.5 cement, P O4. 5R cement,PO. 5ce
ment exceeds 50, made the 30 min uidity re on sham decline, more than 6%of rative P. O525R cement
made 30 min fluidity retention decline sharply; R SA 45 replacing P. O cement mproved 1 d, 3 d strengths, reduce
the 28 d strengths; and the influence of reduce the 8 d strengths on thethe fast hydraulic cements were slightly smad
ler, the non-fast were larger
Key words: cementitious grout; cement; applicability
水泥基灌浆材料是由水泥为基本材料,适量的细骨料及加入少量的混凝土外加剂及其它材料组成的干
混材料,加水拌合后具有大流动度,早强、高强、微膨胀的性能。因其具有无收缩、强度高、自密实、施工方便
等特点,泛应用于设备基础的二次灌浆、地脚螺栓锚固、混凝土修补加固等方面。由于进?灌浆料的价格
昂贵,加之国内需求旺盛,近几年我国对浆料的研究十分活跃并取得了较大进展,在材料的性能和成本方
面都有所突破3。
国内的水泥基灌浆料所用水泥通常是硅酸盐水泥,并通过添加膨胀剂促使水泥浆体内部形成钙矾石,以
获得早强、高强、微膨胀等性能。因钙矾石在80C即会发生分解,有报道担心国内市场上的膨胀剂性能的稳
定性,并因此质疑灌浆料体系在工程应用上的稳定性。
硫铝酸盐水泥具有快硬、早强、微膨胀的特性,可用于配制水泥基灌浆料,但其价格较普通硅酸盐水泥高
出不少?因而有研究使用硅酸盐水泥、硫铝酸盐水泥复合胶凝体系来降低成本回。硫铝酸盐水泥与普通水
泥的适应性有待探讨。该文研究了各种硅酸盐水泥与硫铝酸盐水泥复合胶凝体系的适应性,对相关企业选
择原材料具有一定指导意义。
收稿日期:2013-04-23
作者简介:彭鹏飞(1982-),硕士,工程师.E-mail:pfeil04@163.com
万方数据