辐照交联乙烯-四氟乙烯绝缘航空线制备与性能表征
郑伟,王新营,严波,计初喜2,刘淮平
(1.特种电缆技术国家重点实验室,上海200009:2.上海特缆电工科技有限公司,上海201300)
摘要∷利用开发的四种XEIE绝缘料进行制备航空线试验,观察绝缘料的可加工性能,对航空线进行一系列
剂量的辐照交联加工;对加工制各完成的XEIE航空线进行力学性能与交联度验证测试,以满足ML-W
22759和(GJB773A2000要求。
关键词∷辐照交联;乙烯一四氟乙共聚物;航空线
中图分类号:TM246.9
文献标识码:A
文章编号:16726901(2013)040019-03
The Preparation and Properties of X-E TFE Aircraft Wire
ZHENG Wei, WANG Xin-ying YAN Bo, JI Chu-xi, IU Jingpin
(1. State Key I aboratory of Specialty Cable Technology, Shanghai 200003, China
2. Shanghai Special Cable Teehnology Lld, Shanghai 201300, China)
Abstract. Four types of XETFE insulated materials were processed into aircraft wires, and the wires were treated by
irradiation crosslinking. The processability, mcchanical propertics and crosslinking - test of the wires were stud-
ied. The results showed that the performances of aircraft wires met the requirements of the standards MIL 22759
and G]B 773 A-2000
Key words. irradiation crosslinked, ETFE, aircraft wire
引言
航空线制备
在航空航天用电线电缆中,辐照交联电线有交1.1原材料
联聚氯乙烯绝电线、辐照交联乙烯-四氟乙烯共
上海电缆研究所自制四种 X-ETFE绝缘料,分
聚物( X-ETFE)绝缘电线等,其中 XETFE绝缘电线别为采用进口国外公司ETYE树脂的1#与2#绝缘
正是当今航空用电线中的两种主要线种之
料,采用国内公司EIFE树脂的3#与4#绝料。导
X.TFE绝缘电线采用特殊的X-"TFF绝缘料,体为20AWG线规镀锡铜绞合导体
挤包成电线后,经电子束辐照而交联 X-ETFE除保1.2生产设备
持ETFE原有特性外,其温度等级提高到200℃。该
具体航空线生产在上海特缆电工科技有限公司
电线一般采用薄壁绝缘结构,如单层绝缘电线的绝完成。氟塑料挤出采用5单螺杄高温串挤设备
缘厚度为0.15mm,故在相同载流量要求下,电线重电子加速辐照器2.5MevV。
量轻,这一点对航空航天飞行器来说是非常重要的,1.3生产过程
所以自上世纪70年代以来,这一线种一直深受航空
绝缘料在60~70℃下烘2~3h:制备标准
航天业的青睐,目前无论是军用还是民用航空航天MI.-W22759/32:挤出机温度220~330℃配模工
飞行器都大量使用这种电线。
艺,内模1.5/3.3mm、外模4.5mm;收线速度不超
上海电缆研究所采用国产设备及原材料研发过20m/min;火花电压5.7kV;成品外径1.270±
XETEE绝缘料,并制备出 XETFE绝缘航空电线,0.05mm。
经过一系列性能测试后,所制备的XETE绝缘航
航空线试制过程中,1#与2#绝缘料过程顺利,
空线满足相关标准要求
成品线径控制较为稳定,无击穿现象,且电线表面光
收稿日期:20121114
滑、无缺陷,表观质量优良。
基金项目:国家重点基金研究发展计划暨“973”计划
3#与4#绝缘料生产过程中成品线径误差较大
经过工艺调整后情况未能有明显好转,但线径仍然
作者简介;郑伟(1984-),男,硕土研究生,工程师.
在标准要求的范围内。电线表面光滑,有少量的杂
作者地址:上海市军工路1000号00093
质出现,出现少量击穿现象,国产原料性能和质量稳