应用研究
新型钢锭模硏究与运用
陈培红,潜美丽,靳鹏,许益华,王纪元,姚国平,张应山
(太原重工治铸分公司,山西太原030024)
摘要:根据钢锭模的设计理念,针对现有钢锭模生产的钢锭在生产34 CRMOLA时废品率高的问题,重新设
计了下注三孔底盘钢锭模(三孔模)。运用计算机数值模拟软件,对新设计的三孔绽模进行了充型过程模拟,模
拟结果显示三孔底盘钢锭模结构合理,在实际生产中三孔底盘的钢锭使34 CRMOLA转子的废品率明显降低。
关键词:三孔底盘;钢锭模;注速;计算机数值模拟
中图分类号:TP391
文献标识码:A文章编号:1674-6694(2013)04-0037-03
Study and Application of New Ingot mold
CHEW Pei-ong, AN Mei-li, N Peng, U Yi-hwa, WANG -yuan, YAO Guo-ping, ZHANG Ying-shan
(Taiyuan Heay Industry Smelting and Casting Branch, Taiyuan Shanxi 030024, China
Abstract: According to the design idea of steel ingot mold, by improving the general single hole bottom ingot mold, a new type of
three-hole bottom ingot mold was designed. The advantages of the three hole bottom ingot mold were summed up by comparing the two
ingot molds using computer simulation. in actual production, the application of three hole bottom ingot mold makes the 34CRMO1A rotor
reject rate decrease significantl
Key words: three hole bottom mold, ingot mold, pouring rate, computer simulation
太重冶铸分公司原钢锭锭型的设计参数是上艺参数与缩孔、硫松的关系,从理论上验证设计的
世纪50年代从原苏联引进的。这些锭型属于“高合理性叫。下面是设计的两个主要方面。
瘦”型,高宽比大,锥度小。34CrMo1A采用这样的锭1.1.1改变注速和浇注温度
型生产,废品率高。针对34CrMo1A废品率高,开始
浇注的主要参数是浇注温度和浇注速度,在确
硏究钢锭模参数对钢锭质量的影响,并设计出新型定这两个参数时,除了考虑这两个参数本身外,还
钢锭模。
要考虑二者之间的关系,如何对待这两个参数之间
的关系,目前国内外有两种观点:一是低温快浇,二
试验过程与讨论
是高温慢浇。在国内占主导思想的是低温快浇,在
1新锭模设计过程及参数
这种观点的指导下,进行浇道系统设计,使钢锭的
设计理念:高宽比减小、锥度增加有利于钢锭充型过程更加合理,通过收集和整理大量的资料,
实现自下而上顺序凝固,易于钢水补缩,中心较密设计出新底盘一一三孔底盘。采用三孔底盘,使以
实。然而对于上大下小带保温帽的钢锭,为了减慢前单孔充型变成三孔充型,能够实现较快的充型速
上部钢液的凝固速度,得到更为致密的组织,锥度度,充型时间减短,热量损失减小,可以降低浇注温
还要加大。但钢锭模锥度不能无限放大,合理增大度,实现低温快浇的目的。新三孔钢锭模三维模型
锥度,降低高宽比,依此设计的钢锭模的应用使产见图1,三维图中的所有尺寸参数与实际生产一致。
品废品率有所降低,但仍不能达到合理范围。为了
表1中列出两种三眼钢锭模和普通钢锭模的注
更好地实现上述目的,根据计算及试验结果,对系速,与普通下注钢锭相比,浇注总时间最少减少2min
列锭型尺寸进行优化,并通过计算机模拟,找出工
min,錠身减少1min~2min,冒口减少1min,而
且随着钢锭模变大,这种速度优势将更加明显,我
厂三孔45t钢锭的锭身浇注时间比普通要减少
收稿日期:2013-04-19
作者简介:陈培红(1984-),男,硕士研究生,助理工程师,从事炼钢
以上。浇注时间变短,能减少二次氧化带来的
及钢锭工作。
夹杂。