球墨铸铁件的补缩.pdf

?
铸造工程
Foundry Engi neer ing
球墨铸铁件的补缩
吴忠亮,孟君2,杨均斗1,吕恒,沈奇,张兆宇,聂爽2
(1.沈阳机床西丰铸造有限公司,辽宁铁岭112400:2.沈阳机床银丰铸造有限公司,
辽宁沈阳110003.张店钢铁总厂,山东淄博255000
摘要:结合铸造生产实践,总结了几种行之有效的球墨铸铁件补缩方法,分析了一种有效冷冒
口的作用机制,指出树脂砂芯在金属液的热作用下产生的大量气体进入冒ロ,对其中的金属液
进行了物理搅拌,并与其发生放热化学反应,推迟了冒口颈及冒口本体的凝固进程;当厚大热
节存在于铸件最高处时,冷铁和冒口并用是既经济又有效的エ艺方法
关键词:球墨铸铁;冒ロ;缩孔;缩松;
中图分类号:TG255文献标识码:B文章编号:1673-3320(2014)04-0034-04
Feeding for Ductile Iron Castings
WU Zhongliang MENG Jun, YANG Jundou, LYU Heng, SHEN Qi, ZHANG Zhaoyu NIE Shuang?
1. Shenyang Machine Tool Xifeng Foundry Co, Ltd, Tieling 112400, Liaoning, China,
2. Shenyang Machine Tool Yinfeng Foundry Co, Ltd, Shenyang 110000, Liaoning, China
3. Zhangdian Iron and Steel Works, Zibo 255000, Shandong, China
Abstract: Combined with the production practice of casting, several effective feeding methods for
ductile iron castings were summarized. The mechanism of action for an effective cold riser was analyzed
It's pointed out that the resin sand cores under the thermal effects of molten iron generate a lot of gas
to enter the riser, in which the liquid metal is agitated by gas to occurre exothermic reactions. The
solidification process of metal both in riser and its neck are put off. While a thick hot spot on the top of a
casting, using both a proper riser and some chills is an economical and effective technological process
Key words: ductile iron:; riser; shrinkage dispersed shrinkage
球墨铸铁件的补缩(包括以浇注系统补缩)缩。该铸件重22kg,材质QT500-7,浇注温度
措施是否得当,不仅是获得合格铸件的重要前1350~1370℃,一箱4件,中间注入式浇注,树
提,也是铸造实践中关乎成本和效率的主要设计脂砂手工造型。
内容之一。实践中使用的补缩方法很多,诸如利
支座铸件上部40mm铸出孔内部及其两侧
用浇注系统补缩,以及冷铁和冒口等,可根据不面、孔的上下端面均需进行局部深入加工.。由于
同的铸件结构及其质量要求采取一种或多种工艺该部位厚实、热节大,若不采取措施极易产生缩
方法。本文结合铸造生产实践,对球曌铸铁件的松而使铸件报废。根据以往的经验和一般原则
补缩方法及其作用机制进行了分析和总结。
优先考虑采用热冒口直接对厚实部位进行补缩,
但由于该厚大部位为斜面,位置及形状均很特
1“冷冒口”补缩
殊,实际上很难实现。采取的工艺方案为∮40mm
许多文献都认为冷冒口是不起作用的,孔不铸出,在此部位的炳侧及上下端面均布置明
甚至还会起坏作用1-2]。但笔者曾经在某机床冷铁激冷,以将收缩缺陷留在孔中心部位待加工
支座铸件上成功使用了一个冷冒口对其进行补时去除,不设置补缩冒口;在厚实部位的对面以
收稿日期:2013-12-19
作者简介:吴亮(197
男,工程师,主要从事铸铁件的铸造工艺设计及其生产实战
34「2014年第4期