再生混凝土轴心抗压强度试验研究.pdf

2011年第9期(总第263期
混
凝
理论研究
Number 9 in 201 1(Total No 263)
Concrete
HIEORETICAL RESEARCH
doi:10.3969/js.1002-3550.2011.09.002
再生混凝土轴心抗压强度试验研究
陈宗平12,薛建阳,余兴国2,柯晓军2
(1.福州大学土木工程博士后流动站,福建福州350108;2.广西大学土木建筑工程学院,广西南宁530004
3.西安建筑科技大学土木工程学院,陕西西安710055)
摘要:利用服役50年后的废旧混凝土电杆作为再生粗骨料原料,配制了11种不同粗骨料替代率的再生混凝土,替代率从0-100%变
化,级差10%,一共33个棱柱体试块。在电液侗服试验机上加载试验,观察了其破坏过程和破坏形态,并获取了其荷载一位移全过程曲线。
在试验基础上,对各种骨料替代率再生混凝土的荷载一位移全过程曲线进行分析,研究并提出了其本构方程。结果表明:再生骨料混凝土
与天然骨料混凝土相比,随着骨料替代率的增加,再生混凝土棱柱体抗压强度略有提高,应力应变曲线具有相似的形状,在上升阶段,再生
混凝土与天然混凝土的应力应变曲线变化不大,但在下降段再生混凝土更为陡峭.
关键词:再生混凝士;骨料替代率,轴心抗压强度;应力ー应变关系;本构方程
中图分类号:TU528.0
文献标志码:A
文章编号:1002-3550(2011)09-0004-04
Experimental research on the axial compression strength of recycled coarse aggregate concrete
CHEN Zong-ping", XUE Jian-yang, YU Xing-guo=, KE Xiao-jun
(1. Civil Engineering Post-doctoral Research Station, Fuzhou University, Fuzhou 350108, China
2. College of Civil Engineering and Architecture, Guangxi University, Nanning 530004, China
3. School of Civil Engineering, Xi'an University of Architecture and technology, Xian 710055, China)
Abstract: In order to study the mechanical behavior ofrecycled
te concrete( RAC), 33 RAC prisms specimens(150 mmx150 mmx300 mm)
were mixed, which have 1 1 kinds of different recycled coarse aggregates replacement ercentage RAC specimens, every kind has 3 specimens And the
replacement percentages recycled coarse aggregate from 0 to 100%, the increment is 10% The recycled coarse aggregates come from waste electric
pole concrete( produced in 1958) The failure pattems and loading-displacement curve can be obtained using an electro-hydraulic servo test machine
Based on the experimental results, the stress-strain relationship curve of different recycled coarse aggregates replacement percentage RAC pecimens
are analyzed, and the stress-strain relation calculation formula is obtained. Resarch results show that with the recycled coarse ag egatcs replacement
percentage increasing, he axial compre ion strength of RA have sli l enhancment and he shape of stres-srain relationship curve is similar
between RAC and normal aggregate concrete( NAC), little change in ascending phase, but, in descending, RACIS more precipitous decline than NAC
Key words: recycled aggregate concrete (RAC); replacement percentage; axial compression strength; stress-strain relationship; constitutive
equation
其应力ー应变全过程曲线,分析不同骨料替代率对轴心抗压强度
的影响,并研究确定其应力-应变木构方程,研究结果可为再生
将废旧混凝土经破碎,然后部分或全部代替天然骨料形成混凝土结构的进一步深入研究和推广应用提供参考和依据。
的混凝土,称再生混凝土( recycled coarse aggregate concrete,简
称RAC)。再生混凝土具有节约资源、保护环境等优点,符合可
1试验概况
持续发展战略。对再生混凝土的研究和利用已经成为国内外的
1试验材料
研究热点问题。近年来,各国学者对再生混凝土的各种力学
水泥采用海螺牌P?O32.5R级水泥,砂采用普通天然黄砂,
性能进行了的研究,并取得了一些重要成果,但针对再生粗骨拌合水为自来水,天然粗骨料为连续级配的碎石,最大粒径为
料来源于服役期满(达到设计使用年限)的废旧混凝土的再生20mm。再生粗骨料来源于南方电网1958年生产并且已经服役
混凝土力学性能研究很少。众所周知,混凝土结构达到了设计使50年的废弃混凝土电杅,经破碎和筛分而成,该废弃混凝土电
用年限后,结构的可靠性会降低,必然要拆除,将产生大量的废杆的原来设计强度为C30,并且在破碎前对该批混凝士电杆进
旧混凝土,如何对这些废旧混凝土进行科学处理和再次利用已行回弹试验,废弃混凝土的实测强度为31MPa7,再生粗骨料
经成为一个重要的研究课题。本研究以服役期满的废旧混凝土的最大粒径为20mm,并且在试验前,对再生粗骨料和天然骨
为再生粗骨料来源,进行再生混凝土的轴心受压试验研究,测试料采用同-筛网筛分,均为连续级配。