提高HRB400钢筋屈服强度命中率的研究.pdf

总第222期
炳金
Total No. 222
2014年第6期
HEBEI METALLURGY
2014. Number 6
提高HRB400钢筋屈服强度命中率的研究
张垚,项有兵,薛鹏
(河北钢铁集团唐钢公司第二钢轧厂,河北唐山063016)
摘要:研究了碳、锰、砫、钒对HRB400钢筋屈服强度的影响。通过降低合金料加入量、提高转炉终点碳
含量,实现化学成分的窄范固控制,提高了HRB400钢筋的屈服强度的命中率,同时降低了合金料吨钢
消耗成本。HRB400钢筋适宜的化学成分控制范围是C0.21%~0.23%、Si10.4%~0.5%、Mn1.32%
1.42%、V0.034%~0.038%(HRB400B)和0.029%-0.033%(HRB400D)。
关键词:钢筋;屈服强度;命中率;研究
中图分类号:TG335.6
文献标识码:A
文章编号:1006-5008(2014)06-0022-04
doi:10.13630/j.cnki.13-1172.2014.0606
RESEARCH TO NNCREASE HT RATIO OF
YIELD STRENGTH OF HRB400 REINFORCED BAR
Zhang Yao, Xiang Youbing, Xue Peng
No 2 Steel Rolling Mill, Tangshan Iron and Steel Company, Hebei Iron and Steel Group, Tangshan, He-
bei,063016)
Abstract: The influence of carbon, manganese, silicon and vanadium on the yield strength of HRB400 rein
forced bar is researched. Its hit ratio is increased by reducing amount of alloy materials, increasing end car-
bon content in converter, realizing narrow range control of chemical composition, at the same time the con-
sumption cost of alloy materials per ton of steel lowered. The suitable control range of chemical composition
for HIRE400 reinforced bar is:C0.21%~0.23%,Si0.4%~0.5%,Mn1.32%~1.42%,V0.034%
0.038% for HRB400B or.029%.0.033% for HRB400D
Key Words: reinforced bar; yield strength; hit ratio; research
0引言
定。2014年1~2月,HRB400屈服强度命中率为
为提高建筑用钢的性能、节约钢材用量,我国逐64.91%,其中HRB400B(规格25mm、28
渐用HRB400螺纹钢取代HRB335钢。但是目前生mm、32mm)为42.84%,HRB400D(规格≤22
产的HRB400钢屈服强度普遍较高,存在加入合金mm)为72.92%。通过对影响屈服强度的化学成分
过量的现象。对钢中影响屈服强度化学成分合理范进行分析,研究了HRB400热轧带肋钢筋化学成分
围的研究,以及HRB400屈服强度窄范围控制,在文与屈服强度的关系,提出其含量的合理控制范围,提
献中均未见相关报道。
高了HRB400屈服强度的命中率,进而稳定了钢筋
本文研究的HRB400钢屈服强度命中率指屈服的力学性能,减少了合金加入量,降低了生产成本
强度在420~460MPa的数量占合格钢筋(屈服强
影响屈服强度的化学成分分析
度大于400MPa)数量的比例。唐钢第二钢轧厂具
化学成分对钢筋屈服强度的影响是比较大的。
备年产200万t热轧带肋钢筋的生产能力,近一半而现有治炼水平下各元素的含量范闱控制较宽,造
的钢屈服强度高于460MPa,性能过剩并且不稳成了钢筋屈服强度性能过剩,并且波动较大。因此,
需对化学成分进行窄范围控制,制定了表1中的目
收稿日期:204-04-14
标范围。
作者简介:张垚(1985-),男,助理工程师,2008年毕业于太原理工
大学治金工程专业,现在河北钢铁集团唐钢公同第二钢轧厂从事转
炉炼钢工作,E-mail:zhiyejingli,ren@163.com