海泡石环境吸附材料制备研究.pdf

第39卷第4期
非金属矿
Vo.39 No, 4
2016年7月
Non-metallic Mine
July, 2016
海泡石环境吸附材料制备研究
张韬贺洋
(苏州中材非金属工业设计研究院有限公司,江苏苏州215004)
摘要利用海泡石原矿,通过选矿提纯和精细加工等处理,制备了海泡石空气吸附材料;采用元素分析、比表面积、SEM、XRD等方法对制
备的材料进行了表征。结果表明:该海泡石空气吸附材料海泡石含量高、比表面积大,对甲醛等有害气体吸附效果明显
关键词海泡石;提純;活化;吸附;甲醛
中图分类号:TQ424.24文献标识码:A文章编号:10009098(2016)04-0046-02
Environmental Adsorbing Material Prepared by Sepiolite
Zhang Tao He Yang
(Suzhou Sinoma Design&Research Institute of Non-metallic Mineral Industry, Suzhou, Jiangsu 215004)
Abstract The adsorbing materal for air purifcation was ob ined through urification and elaboration processes of raw sepiolite. The adsorbing
material was characterized by elemental analysis, BET, SEM, XRD. The results showed that the material has strong absorbability of formaldehyde etc,
with high surface area and high content of sepiolite
Key words sepiolite; purification: activation adsorption formaldehyde
海泡石是一种纤维状富镁黏土矿物,属链状结1.2样品制备
构,在链状结构中又含有层状结构的小单元,属2:11.2.1海泡石原矿提纯:采用螺旋分级机除砂,水力
层型。由于海泡石具有这种特殊的孔道结构,因而比旋流器抛尾,卧式离心机精选的提纯工艺,工艺流程
表面积和孔体积很大,有极强的吸附、脱色和分散等为:海泡石原矿→捣浆→螺旋分级→旋流器分级→离
性能,而且质轻、化学稳定性好,自身存在大量酸碱中心机提纯→海泡石精矿。
因此广泛用于吸附剂催化剂载体、过滤剂等
首先,将海泡石原矿配成质量分数为10%的矿
针对室内空气污染,发展高效环保吸附材料是浆,加入六偏磷礫酸钠,高速搅拌30min,然后采用螺旋
解决这一问题的重要方式,而本身具有优良吸附性能分级机进行除砂;矿浆进内径为75mm水力旋流器
的矿物是制备吸附材料的理想原料。相对于活性炭,进行分级,抛除大部分粗尾矿;接下来旋流器溢流进
海泡石是一种能源消耗低、不容易燃烧,而且可以回卧式离心机分级,精选得到海泡石精矿;最后海泡石
收利用,无二次污染的材料,同时具有优先吸附甲醛、矿浆加入聚丙烯酰胺经过絮凝、压滤、干燥,即得到海
苯、总挥发性有机化合物(TVOC)等有害气体的特泡石粉体。
点。所以,海泡石广泛应用于装修污染洽理、家居除1.2.2海泡石活化改性:取一定量的提纯海泡石精矿
异味和汽车内空气净化,是一种发展前景广阔的环境在反应釜中配制成质量分数为12%的矿浆,按海泡
友好型新材料,利用海泡石制备空气吸附材料对室内石精矿质量百分数409%向反应金中加入相应的硫酸,
空气治理具有重要意义
在80℃下搅拌反应8h;然后将矿浆洗涤、过滤、干燥,
实验部分
即得到活化海泡石?。
1.1原料及试剂原料:湖南湘潭的短纤维海泡1.2.3海泡石吸附材料成型:活化海泡石与成孔材
石原矿,颜色呈深灰色,其化学组成(w0)为:SiO2,料按1:100的质量比复合,经圆盘造粒机成型,在
64.45;Al2O3,7.32;Fe2O32.5;K、O,0.42;Na2O,0.15;280℃下煅烧得到海泡石空气吸附产品。
MgO,11.90;CaO,3,45;TiO2,0.35;烧失量,903。试剂:1.3样品表征采用马尔文激光粒度仪测定粒度;
六偏磷酸钠,分析纯,市售;聚丙烯酰胺,分析纯,市采用JW-BK静态氮吸附仪测定样品的比表面积;采
傳;硫酸,分析纯,市售;甲醛,分析纯,市售。
用日本日立电子公司S-3500N扫描电子显微镜观察
海泡石的微观形貌;采用荷兰X'per型X射线行射
收稿日期:2016-06-13
仪测定海泡石的物相组成
46