高温作用下新型化学锚栓极限抗拔承载力试验研究.pdf

.ututu.com2010年第8期(总第250期)混凝土原材料及輔助物料Number 8 in 2010(Total No250)ConcreteMATERIAL AND ADMINICLEdoi:10.3969/5.iss:1002-3550.2010.08.024高温作用下新型化学锚栓极限抗拔承載力试验研究那国起(坊学院建筑工程学院,山东濰坊261061)摘要:介绍了一种新型化学铺栓,通过研究高温作用下影响新型化学锚栓极限锚固力的3种因素:温度冷却方式、静置时间,得出如下研究结论:随温度升高,新型化学锚栓的极限抗拔承载力先降低后回升再大幅度降低;自然冷却的极限抗拔承载力高于浇水冷却;随静置时阿延长,极限抗拔承载力降低幅度较小。关键词;新型化学锚栓;高温作用;冷却方式;静置时间:极限抗拔承载力中图分类号:TU528.01文献标志码:A文章编号:1002-3550(2010)08-0071-02ultimate uplift capacity experivent study of new type chemical anchoring bolts under high temperatureXING Guo-qiCollege of Civil Engineering, Weifang University, Weifang 261061, ChinaAbstract: It introduces a new type chemical anchor bolt. It studies three factors impacting anchoring force of new type chemical anchoring boltsunder high temperature: temperature, cooling way, standing time. It draws conclusions of the study that ultimate uplift capacity begin to reduce andthen raise and then reduce significantly with increasing mperature and ultimate uplift capacity of natural cooling is higher than that of wateringcooling and uitimate uplift capacity reduces lesser extent with the extension of standing time.Key words: new type of chemical anchoring bolts; high temperature; cooling way; standing time; ultimate uplift capacity0引言混凝士后锚固技术现已成为我国工程建设中一种不可缺少的新型技术。化学锚栓(图1)是混凝土后锚固技术的一种形式,主要应用于幕墙或干挂石材等连接件铺固方面。化学锚栓由化学胶管与螺杅等组成,化学胶管一般由胶黏剂、固化剂和骨料组成,胶黏剂大多为热固性有机高分子材料,有机高分子材料耐高温性能较差,热变形温度约为80,化学锚栓在某些情况难以满足焊接要求。针对化学锚栓不耐高温的缺陷,国外化学铺栓生产厂家如喜利得、慧鱼等研制开发了耐高温的化学错栓,但价格较高,在我国大面积推广使用存在困难。针对上述图1化学栓化学错栓存在的问题,研制了一种质优价廉的新型化学锚栓。新型化学锚栓与传统化学锚栓不同之处是药剂管的不同,新型化学锚栓采用最新研制成功的锚固剂一无机化学药包剂代替药剂管,药包剂采用特殊工艺生产的纸将无机化学材料包装成条形并密封(图2)。无机化学药包剂的组成材料无毒且不会对环境造成污染,材料自身的特性决定了无机化学药包剂具有比传统化学锚栓优越的耐高温性能。主要考虑温度、冷却方式及静置时间,对高温作用下新型化学锚栓极限抗拔承载力进行研究,为新型化学锚栓的设计与应用提供依据。1试验概况5?图2新型化学锚栓定例,采用先加热后加载的方法,对新型化学锚栓构件连续加热1.1试验方法到指定温度-100、200、300、500、700、900門,然后来用不同根据GB/T9978-1990建筑构件耐火试验方法的相应规的冷却方式冷却一一自然冷却和浇水冷却,经不同的静置时间收稿日期:2010-0314基金项目:滃坊学院青年科研基金项目(2009Z12)