研究开发
多孔二氧化钛吸附刚果红
刘凤艳,肖丽伟2,康志成2,王妍姗2,白瑞珠2,胡鑫2
(鞍山工业研究院,辽宁鞍山114011:2浙江师范大学化学与生命科学学院,浙江金华321004
摘要:以异丙醇钛为前体,十二烷胺为模板剂,采用配体辅助模板法合成高比表面积多孔二氧化钛材料,利用
气吸附对其孔径性质进行分析。通过静态吸附实验研究了多孔二氧化钛对刚果红的吸附行为,考察了吸附时
间、温度、搅拌速度、吸附剂用量和初始浓度对刚果红吸附效果的影响。分别在相关条件下,结果表明:当吸
附时间为30min时,脱除率达98%以上;吸附温度为45℃时,脱除率可达98%;摇床转速为l60r/min时,脱除
率达到最大;当吸附剂使用量为0.1g时,脱除率能够达到98%左右,已能够满足应用要求;多孔二氧化钛吸附
刚果红的吸附量与刚果红初始浓度成正比。
关键词:多孔介质;二氧化钛;吸附;刚果红;影响因素
中图分类号:TQ069文献标志码
文章编号:1000-6613(2014)05-1321-06
DOI:10.3969iss.100-6613.2014.05.041
Adsorption of Congo Red by Porous Tio2
LIU Fengyan XIAO Liwei, KANG Zhicheng WANG Shanshan, BAI Ruizh, HU Xin
(Anshan Industrial Research Institute, Anshan 114011, Liaoning, China; College of Chemistry and Life Sciences
Zhejiang Normal University, Jinhua 321004, Zhejiang, China)
Abstract: Porous Titanium oxide was synthesized by a ligand assisted template method using
docecylamine as the template and titanium isopropoxide as the precursor. The as-synthesized titanium
dioxide was characterized by nitrogen adsorption. The adsorption behavior of Congo Red by the porous
Tio was studied by static adsorption experiment. The effects of adsorption time, temperature, stirring
speed, adsorbent dosage and initial concentration of Congo Red on the adsorption performance were
investigated. Results showed that when the adsorption time reached 30 min, the removal rate can be
more than 98%: when the adsorption temperature was 45C, the removal rate can reach 98%; when the
stirring speed was 160 r/min, the removal rate was the maximum; when the catalyst dosage was 0.10 g
the removal rate can reach 98%, which met the requirements of application; the Congo Red adsorption
capacity by porous titanium dioxide was found to be proportional to the initial concentration of Conge
Red solution
Key words: porous media; titanium dioxide; adsorption; Congo Red; affect factors
我国染料产量居世界前列,近年来纺织染料工致畸),不仅造成水环境的污染,而且因此危害人类
业迅猛发展,现如今我国各种染料总产量已达90健康?,所以治理染料废水是迫在眉睫的事。现今
万吨,染料总产量约占世界的60%。染料带来多很多染料废水具有抗光解、抗氧化的特点,逐渐増
彩的颜色的同时,不仅产生了经济效益,也产生了大了处理染料废水的难度+
大量废水,并且每年以1%的速度逐年增加2。染料
收稿日期:2013-11-01;修改稿日期:2013-12-30
废水组成复杂,其有机污染物含量高、生物毒性强、第一作著及联系人:刘凤艳(93-),女,高级工程师,主要从事精