内容摘要:
第23卷第3期
材料科学与工艺
Vol 23 No. 3
2015年6月
MATERIALS SCIENCE &TECHNOLOGY
Jun.2015
doi:10.11951/j.i.1005-0299.20150304
拉深比对304不锈钢圆筒件残余应力的影响
肖良红,龙涛,徐俊瑞,王欢
湘潭大学机械工程学院,湖南湘潭411105
摘要:304不锈钢圆筒拉深件在其口部易发生纵向开裂,外壁残余拉应力过大是造成其纵向开裂的根本原因之ー.本文
结合有限元法分析不同拉深比所得圆简拉深件的残余应力,用纳米压痕试验研究了拉深比对304不锈钢圆筒拉深件筒壁
残余应力的影响.结果表明:304不锈钢圆筒拉深件外壁的残余拉应力从筒底到口部先增大后减小,最大残余应力出现在筒
壁中部约(60%筒壁高度处;纳米压痕测得拉深比为1.43、1.54、1.67和1.82拉深圆筒件筒壁的最大残余应力分别为391.87
745.30、793.74和1013.1MPa;最大残余应力随拉深比的增大而增大.与其他文就对比分析,此研究结果是正确可靠的
关键词:304不锈钢;圆简拉深件;残余应力;纳米压痕;有服元模拟
中图分类号:TG335.4:;TG306
文献标志码
文章编号:1005-0299(2015)03-0018-06
Influence of drawing ratio on the residual stress in 304 stainless steel
cylindrical drawing parts
XIAO Iianghong, LONG Tao, XU Junrui, WANG Huan
School of Mechanical Engineering, Xiangtan University, Xiangtan 411105, China)
Abstract Iongitudinal cracking easily happens in the mouth of 304 stainless steel cylindrical drawing parts, where
one of the essential reasons is due to the large residual tensile stress in their outer wall. Combined with finite
element analysis, the influence of the drawing ratio on residual stresses in 304 stainless steel cylindrical drawing
cups wall was studied in this paper by nanoindentation tests. The main contents and results are as follow: The
residual tensile stress in the outer wall of 304 stainless steel cylindrical drawing cup increased first and th
decreased from the cup bottom to its mouth. The maximum residual stresses always appeared in the middle of the
cylindrical cups wall along the height direction about at 60% wall height from the cup bottom. The maximum
residual stresses in the outer wall of cylindrical cups with ifferent rawing ratios of 1. 43, 1.54, 1.67 and 1.82 were
391.87, 745.30, 793.74 and 1 013. 1 Mpa respectively, which were tested by nanoindentation. They increased with
the drawing ratio. By analysis and comparison of the reported literatures, the results were correct and reliable
Keywords: 304 stainless steel; cylindrical rawing arts; residual stress; nanoindentation; finite element simulation
拉深成形是一种基于塑性变形的板料冲压成和耐腐蚀性能,在各行各业中被广泛地应用.但不
形工序.残余应力普遍存在于塑性成形的工件中,锈钢制品会因为应力腐蚀开裂而失效,严重影响
它随材料性质、工件的形状和尺寸、加工工艺参数其使用寿命及安全.为确保工件使用的安全性,
的不同而不同.构件中的残余应力对其疲劳寿命、防止残余应力造成不必要的损失,许多科技工作
强度、尺寸和形状精度及稳定性都有很大影响.者已把如何抑制或消除被加工件内部的残余应
304不锈钢具有优异的综合力学性能、加工性能力、调整或改变被加工件中残余应力的最终分布
作为研究重点,并先后开发了许多评估残余应
收稿日期:2014-10-3
力的方法,如悬臂梁法“、钻孔法?、鼓泡法?、
基金项目:国家自然科学基金资助项日(51175445)
作者简介:肖良红(1968-),男,博士,副教授
射线衍射法”?、拉曼光谱法、压痕法?、切环